Structural and Dielectric Studies of Fe-Li Substituted Hexagonal Barium Titanate

PG Bhatia

We have studied the influence of a new lead-free Fe/Li incorporated H-Bt prepared by the solid state reaction method and compared it with pure hexagonal barium titanate. The hexagonal phase was stabilised at room temperature due to substitution with Fe-Li. Lattice constants were refined as a = 5.720 A.U., c = 13.96 A.U. Both XRD and IR imply that Li enters octahedral as well as Ba sites. Dielectric measurements show an increase from 800 to 105 indicating sample to be potential colossal dielectric constant (CDC) material. Abnormal grain growth (AGG) was restricted in the substituted sample and normal grain growth was observed.

నిరాకరణ: ఈ సారాంశం ఆర్టిఫిషియల్ ఇంటెలిజెన్స్ టూల్స్ ఉపయోగించి అనువదించబడింది మరియు ఇంకా సమీక్షించబడలేదు లేదా నిర్ధారించబడలేదు

ఇండెక్స్ చేయబడింది

Academic Keys
ResearchBible
CiteFactor
కాస్మోస్ IF
RefSeek
హమ్దార్డ్ విశ్వవిద్యాలయం
వరల్డ్ కేటలాగ్ ఆఫ్ సైంటిఫిక్ జర్నల్స్
విద్వాంసుడు
ఇంటర్నేషనల్ ఇన్నోవేటివ్ జర్నల్ ఇంపాక్ట్ ఫ్యాక్టర్ (IIJIF)
ఇంటర్నేషనల్ ఇన్స్టిట్యూట్ ఆఫ్ ఆర్గనైజ్డ్ రీసెర్చ్ (I2OR)
కాస్మోస్

మరిన్ని చూడండి